Inconel 690传热管GTAW对接焊接头组织及力学性能研究

对Inconel 690传热管材进行钨极气体保护焊(GTAW)对接焊,采用拉伸试验机、压扁试验机和光学显微镜测试和分析传热管焊接接头,同时利用ANSYS软件开展焊接接头在设计工况失压时的一次应力强度校核。研究结果表明:焊缝中心为树枝胞状晶,熔合线附近为粗大柱状晶。室温时接头的平均抗拉强度为619 MPa,平均屈服强度为292 MPa,350℃时接头平均抗拉强度为475 MPa,平均屈服强度为206 MPa,拉伸接头断裂从熔合区开始贯穿整个焊缝组织,呈塑性断裂。压扁试验和反向压扁试验结果表明管接头完好。通过ANSYS分析可知,设计工况下传热管接头350℃许用应力强度150 MPa限值可满足其一次应力强度要求,且裕量较大。     

Metal chlorides-promoted ammonia absorption of deep eutectic solvent

Ammonia is considered as a promising hydrogen or energy carrier. Ammonia absorption or adsorption is an important aspect for both ammonia removal, storage and separation applications. To these ends, a wide range of solid and liquid sorbents have been investigated. Among these, the deep eutectic solvent (DES) is emerging as a promising class of ammonia absorbers. Herein, we report a novel type of DES, i.e., metal-containing DESs for ammonia absorption. Specifically, the NH₃ absorption capacity is enhanced by ca. 18.1–36.9% when a small amount of metal chlorides, such as MgCl₂, MnCl₂ etc., are added into a DES composed of resorcinol (Res) and ethylene glycol (EG). To our knowledge, the MgCl₂/Res/EG (0.1:1:2) DES outperforms most of the reported DESs. The excellent NH₃ absorption performances of metal–containing DESs have been attributed to the synergy of Lewis acid–base and hydrogen bonding interactions. Additionally, good reversibility and high NH₃/CO₂ selectivity are achieved over the MgCl₂/Res/EG (0.1:1:2) DES, which enables it to be a potential NH₃ absorber for further investigations.     

Structural modification of aminoclay for catalytic applications

Abstract

An eco-friendly catalyst system was synthesized using three step reaction. The Cu nanoparticles bridged aminoclay catalyst was analyzed using various analytical techniques. The structure of the catalyst was confirmed by FTIR and XRD. The synthesized catalyst system was used for the reduction of p-nitrophenol (NP), Cr(VI), and fluorescein (Flur) dye individually, as well as in their mixture forms. The k_app value was computed to access the efficiency of the catalyst. The results indicated that the k_app value of the individual system is higher than that of the mixture systems due to the absence of the complex formation reaction. The catalytic performance of the catalyst was also tested for the Schiff base (SB) formation between poly(ethyleneglycol) (PEG) and aniline (ANI) in an oxygen atmosphere. The ¹H-NMR spectroscopy result indicates that the present catalyst system produced 86% yield.     

智能化救援监控系统在煤矿安全生产中的应用

针对煤矿发生事故后传统救援监控系统无法实时对井下人员进行动态定位，导致矿井救援盲目性大、救援效率差、救援难度大等技术难题，为了进一步提高煤矿救援效率，通过技术研究，设计了一套以通信基站为核心的智能化救援监控系统，分析了该系统结构组成、工作原理，通过在担水沟煤矿井下实际应用效果来看，智能化救援监控系统对人员定位精准度达95%，实现人员动态位置三维成像，救援效率提高至80%以上，有效缩短了煤矿事故救援时间，取得了显著应用成效。     

基于步冷试验的2.25Cr-1Mo-0.25V钢母材及焊缝回火脆化研究

对原始态、步冷态、脱脆态和脱脆步冷态2.25Cr-1Mo-0.25V钢母材及焊缝冲击试验结果进行分析,得到了母材和焊缝在不同状态下的韧脆转变温度vTr54.2和FATT以及脆化度ΔvTr54.2和ΔFATT。试验结果表明,步冷试验之后,母材发生较低程度脆化或脱脆现象,但是脆化度或脱脆度较低,表明母材具有良好的抗回火脆化性能;经脱脆试验后,母材和焊缝都发生较高程度的脱脆,表明材料的脆化主要是由于回火脆化引起的,脱脆试验使得材料的韧脆转变温度降低;脱脆步冷试验后,焊缝发生较高程度的脆化,焊缝对脱脆步冷试验的敏感性较高,脱脆步冷试验有效促进了焊缝的脆化。在相同脆化条件下,母材的脆化敏感性低于焊缝,焊缝更易发生脆化。     

福建某低品位金矿新型浸金剂浸金试验

福建某斑岩型金矿品位低、规模大,金主要以自然金形式存在,可见金的粒度较粗,为高效利用该低品位金矿,开展新型浸金剂金蝉全泥浸出试验和柱浸试验,结果表明：全泥浸出在磨矿细度为-0.074 mm占80%、矿浆浓度25%、加石灰调pH 值11.0左右、初始金蝉浓度为500 mg/L和过程中控制金蝉浓度不小于300 mg/L条件下浸出20 h,金的浸出率为93.43%,金蝉耗量为1.02 kg/t；柱浸在矿石粒度为-30 mm条件下喷淋浸出23天,金累计浸出率和金蝉累计耗量分别为86.54%和1.22 kg/t。     

因素空间理论下基点分类算法研究

目前，基于因素空间理论的背景基提取算法计算过程复杂，初始化必须依赖各因素极值，基点数量提取冗余等原因，未能在应用中取得很好效果。为此，结合内点判别法和知识可继承、可扩展的思想，提出一种计算简单、初始化独立、基点数量小的改进的背景基提取算法。然后，利用改进的背景基提取算法构造出一种全新的数据分类算法-基点分类算法，基点分类算法以提取每一类样本的背景基为预测模型，再通过新定义的λ-背景基，优化预测模型。数值实验表明:基点分类算法原理简单、构造难度小、分类模型泛化能力强，预测能力准确率高，同时严格的模型限定区域又能为识别新类别提供新方法。     

阳离子型高温酸化缓蚀剂的合成及其性能评价

针对Mannich碱型缓蚀剂存在的溶解性不好和缓蚀率不高等问题,以甲醛、环己酮和苯胺为原料,合成了一种Mannich碱型缓蚀剂CH-9,将其阳离子化后,再与丙炔醇复配,得到了阳离子型高温酸化缓蚀剂CH-10。由室内性能评价可知,CH-10在盐酸中有良好的溶解分散性;与酸液中其他添加剂如粘土稳定剂和铁离子稳定剂的配伍性良好,不会对酸化地层造成堵塞;在90℃和常压下,在20%HCl溶液中加入浓度为1%的CH-10,其对N80钢片的腐蚀速率为4.765g/(m2·h);在120℃时,浓度为2%的CH-10对N80钢片的腐蚀速率为14.30g/(m2·h),均达到了SY/T5405-1996标准中的一级标准。     

大庆油混兑俄罗斯油对润滑油基础油生产及性质的影响

与大庆原油相比,大庆原油混兑8%俄罗斯原油后,对润滑油基础油的生产和质量均产生了较大影响。基础油HVI 150、350、650的粘度指数下降了1~4个单位,旋转氧弹上升了19~47 min,比色上升了0.5个单位。基础油综合收率提高了0.04%。大庆原油混兑8%俄罗斯原油后,通过调整润滑油生产装置的操作条件,可以生产符合Q/SHR 001-95标准的HVI 150、350、650基础油。